蓝桉树皮化学成分及其液化工艺分析Analysis of Chemical Components and Liquefaction Process of Eucalyptus globulus Bark
刘勇军,史洪洲,汪扬媚,文静
LIU Yong-jun,SHI Hong-zhou,WANG Yang-mei,WEN Jing
摘要(Abstract)：
对5年生蓝桉树皮进行液化处理,对比分析液化前后蓝桉树皮及其液化残渣的化学成分,以探究蓝桉树皮最佳液化工艺。化学成分测定结果表明,蓝桉树皮纤维素、半纤维素和木质素含量为分别为36.65%、18.98%和45.37%,苯醇抽提物、热水抽提物和1%NaOH抽提物含量分别为10.30%、7.15%和23.64%,灰分含量占7.49%。液化工艺研究表明,浓硫酸催化效果明显优于浓磷酸;蓝桉树皮最佳液化工艺参数为:催化剂为3%浓硫酸,温度为160℃,固液比为1∶5。在该液化条件下,蓝桉树皮液化率为82.8%,液化残渣与原料相比,纤维素含量减少了17.90%,半纤维素含量减少了9.19%,木质素含量减少了15.99%。
For 5-year-old Eucalyptus globulus, the optimal liquefaction bark process was explored by analyzing the chemical components of the bark and its liquefaction residue before and after the liquefaction. The results of chemical component determination showed that the contents of cellulose, hemicellulose and lignin of bark were 36.65%, 18.98% and 45.37%, respectively. The contents of benzene-alcohol extractives, hot-water extractives and 1% NaOH extractives were 10.30%, 7.15% and 23.64%, respectively. The content of ash accounted for 7.49%. The liquefaction process showed that the catalytic effect of concentrated sulfuric acid was better than concentrated phosphoric acid. The optimum liquefaction parameters were catalytic of 3% concentrated sulfuric acid, temperature of 160 ℃ and liquid-solid ratio of 5∶1. The liquefaction rate was 82.8% under above optimal conditions. Compared with raw materials, the cellulose content, hemicellulose content and lignin content of liquefaction residue reduced by17.90%, 9.19% and 15.99%, respectively.
关键词(KeyWords)：
桉树;树皮;化学成分;液化
Eucalyptus;Bark;Chemical composition;Liquefaction
基金项目(Foundation): 土壤重金属污染生态修复
作者(Author):
刘勇军,史洪洲,汪扬媚,文静
LIU Yong-jun,SHI Hong-zhou,WANG Yang-mei,WEN Jing
DOI: 10.16779/j.cnki.1003-5508.2019.05.009
参考文献(References)：
- [1]熊济华，四川植物志第八卷/206．桃金娘科MYRTACEAE-1桉属[M].1990,12:305．
- [2]杨新兴，冯丽，华尉鹏．我国能源开发利用的出路与前景[J]．前沿科学(季刊)2012,2.6(22):22~29．
- [3]傅深渊，马灵飞，李文珠．竹材液化及竹材液化树脂胶性能研究[J]．林产化学与工业，2004,24(3):42~46．
- [4]Kobayashi M,Tukamoto K,Tomita B.Application of liquefied wood to a new resin system-synthesis and properties of liquefied wood epoxy resins[J].Holzforschung,2000,54(1):93~97．
- [5]傅深渊，余仁广，杜波等．竹材残料液化及其液化物胶粘剂的制备[J]．林产工业，2004,31(3):35~38．
- [6]张玉苍，迟青山，孙岩峰等．木材液化及其在聚氨酯胶黏剂上的应用研究[J]．林产化学与工业，2007,27(5):73~77．
- [7]Lin L Z,Yao Y G,Yoshioka M,et al.Preparation and properties of phenolated wood phenol formaldehyde cocondensed resin[J].Journal of Applied Polymer Science,1995,58(8):1297~1304．
- [8]Alma M H,Yao Y G,Yoshioka M,et al.The preparation and flow properties of HCl catalyzed phenolated wood and its blends with commercial novolak resin[J].Holzforschung,1996,50(1):85~90．
- [9]Lee S H,Yoshioka M,Shiraishi N.Resol-type phenolic resin from liquefied phenolated wood and its application to phenolic foam[J].Journal of Applied Polymer Science,2002,84:468~472．
- [10]王春明，崔立东，张晶．木材液化的发展现状及研究前景[J]．林业科技，2007,32(3):42~43．
- [11]揭淑俊，张求慧，赵广杰．木材溶剂液化技术及其在制备高分子材料中的应用[J]．林产化工通讯，2005,6:43~49．
- [12]张求慧，赵广杰．我国生物质废料液化及产物利用的研究进展[J]．林产化工与工业，2009,1:120~126．
- [13]许宇星，陈少雄．不同密度桉树能源林数量成熟龄与经济效益的关系[J]．中南林业科技大学学报，2013,2:61~65．
- [14]杨民胜，昊志华，陈少雄．桉树的生态效益及其生态林经营[J]．桉树科技，2006,6:1~23．
- [15]李志辉，杨民胜，陈少雄．桉树引种栽培区区划研究[J]．中南林学院报．2000,3:1~10．
- [16]陈少雄，李志辉．不同初植密度的桉树人工林经济效益分析[J]．林业科学研究，2008,2:1~6．
- [17]符韵林，蓝玉姣．桉树树皮化学成分分析[J]．安徽农业科技，2012,15:8485+8514．
- [18]符韵林，莫引优，覃冠利等．桉树树皮液化及液化物的树脂化[J]．浙江农林大学学报，2011,3:466~471．
- [19]吴嘉恩，刘自力．桉树废弃物催化液化及液化产物树脂化的研究[C].2010-第六届全国化学工程与生物化工年会．
- [20]吴嘉恩，刘自力．无机酸催化桉树废弃物液化性能研究[C].2010-第七届全国工业催化技术及应用年会．
- [21]左志越，蒋剑春，徐俊明．木屑酸催化多元醇液化特性研究[J]太阳能学报，2011,12:1730~1734．
- [22]左志越，蒋剑春．亚超临界乙醇条件下杨木屑与甘油共液化研究[J]．纤维素科学与技术，2011,3:22~27．
- [23]杨丹，袁兴中．塑料和木屑的共液化以及催化液化实验研究[J]．太阳能学报，2010,6:676~671．
- [24]戴伟娣，许玉．亚临界乙醇条件下的纤维素热化学液化研究[J]．太阳能学报，2012,2:249~252．
- [25]刘玉环，王应宽．玉米秸秆常压快速液化最佳工艺参数研究[J]．农业机械学报，2012,6:110~115．
- [26]陈少雄，刘杰锋．桉树生物质能源的优势、现状和潜力[J]．生物质化学工程，2006,1:119~128
- [27]张玉苍，迟青山．木材液化及其在聚氨酯胶黏剂上的应用研究[J]．林产化工与工业，2007,5(27):73~77．
- [28]张求慧，赵广杰．木材的苯酚及多羟基醇液化[J]．北京林业大学学报，2003,6(25):71~76．
- [29]张求慧，赵广杰．木材液化技术研究现状及产业化发展[J]．木材工业，2005,3(15):5~7+11．
- [30]傅深渊，余仁广．竹材残料液化及其液化物胶粘剂的制备[J]．林产工业，2004,6:35~38．
- [31]林小珠，林成辉．开发桉树作为生物质能源的思考[J]．能源与环境，2006,4:106~107
- [32]芋耀贤，梁凌云．基于农作物秸秆的环境友好材料研究-玉米芯液化优化工艺的试验[J]．农机化研究，2008,2:196~199